Hot-dip galvanized wire production line
Design conditions:
1. Wire specification: Φ1.4~5.0mm;
2. Steel wire material: low carbon steel wire such as ASTM1006/ASTM1008
3. Weight of zinc layer: 40~80g/m2
4. Galvanizing speed: the maximum DV value is 80mm.m/min
5. Steel wire strength: 450~550 MPa
6. Number of steel wires: 12
7. Steel wire spacing: 40mm
7. Production capacity: about 22T/D (Φ3.0mm, DV value 70, 24 hours accounting)
About 10T/D (Φ1.4mm, DV value 70, 24 hours accounting)
8. Production line elevation: 900mm
9. Pay-off method: passive pay-off of the spool
10. Take-up method: inverted plum blossom take-up
Production Process :
I-wheel passive pay-off → steel wire heat treatment furnace → steel wire air cooling → tempered water cleaning → turbulent smokeless pickling → overflow water cleaning → assisting plating → hot air drying treatment → hot dip galvanizing → wiping → cooling → inverted Style plum blossom.
 |  |
Hot-dip galvanized wire production line
Design conditions:
1. Wire specification: Φ1.4~5.0mm;
2. Steel wire material: low carbon steel wire such as ASTM1006/ASTM1008
3. Weight of zinc layer: 40~80g/m2
4. Galvanizing speed: the maximum DV value is 80mm.m/min
5. Steel wire strength: 450~550 MPa
6. Number of steel wires: 12
7. Steel wire spacing: 40mm
7. Production capacity: about 22T/D (Φ3.0mm, DV value 70, 24 hours accounting)
About 10T/D (Φ1.4mm, DV value 70, 24 hours accounting)
8. Production line elevation: 900mm
9. Pay-off method: passive pay-off of the spool
10. Take-up method: inverted plum blossom take-up
Production Process :
I-wheel passive pay-off → steel wire heat treatment furnace → steel wire air cooling → tempered water cleaning → turbulent smokeless pickling → overflow water cleaning → assisting plating → hot air drying treatment → hot dip galvanizing → wiping → cooling → inverted Style plum blossom.
| |